Die retaining element

ABSTRACT

An improved die retaining element has a highly efficient, durable and wear and abrasion resistant flange portion surrounding an opening for securing a die mold therein. The flange portion may have practically any geometric configuration, such as round, but is most effective when in a continuous plane with the powder feed box in sliding contact with a feed box. In particular, the flange portion may selectively have either a high precision tetragonal zirconia polycrystal (TZP) ceramic or zirconia-alumina ceramic composite, depending on the surface material of the feeder box in sliding contact therewith. In one embodiment, the flange portion has tetragonal zirconia polycrystal ceramic and the feeder box has zirconia-alumina ceramic composite sliding surface. In another embodiment, flange portion has a zirconium-alumina ceramic composite sliding portion and the feeder box has a tetragonal zirconia polycrystal ceramic sliding portion.

TECHNICAL FIELD

This invention relates generally to an improved die retaining element. More particularly the invention concerns a die retaining element useful for molding equipment having high precision, durable, wear resistant tetragonal zirconia polycrystal (TZP) ceramic and zirconia composite elements.

BACKGROUND OF THE INVENTION

In compression molding operations, efficient filling of the molds with materials in the powder form has a significant bearing in determining the unit manufacturing cost (UMC). Feeder boxes arc used to carry loose powder to the top of the die where it shakes dropping powder into the die cavity. The die cavity is located underneath the die clamp ring or the die retaining ring. The die cavity is filled by the shaking motion of the feeder box which is connected to a hydraulic actuated cylinder. The feeder box slides on a flat surface called "ware plate" in a reciprocating motion. The time interval between the two extreme locations of the feeder box, when the compacting of the powders in the die cavity is effected. The top surfaces of the ware plate, the die retaining ring and the bottom surface of the feeder box need to be at the same level for the smooth operation of the powder filling mechanism. When the die cavity is filled with powder, it is compressed by the action of punches making a "green part". The proper filling of the die cavity depends, among several other factors, on the sliding motion of the bottom of the feeder box on a plate normally known as feeder box ware plate and also on the die clamp (or retaining) ring. If there is a misalignment of the feeder box with respect to the ware plate and also with respect to the die clamp (or retaining) ring or if there is a slight gap between those components, excessive powder loss results. This problem is magnified if the powder particles are very fine (submicron) or are very hard. In such cases, the jamming of the feeder box (in worst case, breakage of the feeder box or ware plate or die clamp ring) can lead to interruption of the manufacturing process and a higher UMC for the part.

Misalignment of the feeder box with respect to the ware plate and/or with respect to die clamp ring can occur due to gouging of one of the surfaces, which is a common occurrence in industrial compression molding machines where the box and the plate and also the clamp ring are usually made of steels. Repeated sliding of two surfaces of metal parts, as in this specific case of surfaces of feeder box and the ware plate (or die clamp ring), usually leads to excessive wear and abrasion of those surfaces leading to the loss of materials, contaminating the powder feed, and also creating a gap between the box and the plate and also between the feeder box and the die clamp ring. This gap between the feeder box and the ware plate and also between the feeder box and the die clamp ring leads to the loss of powder, and in some cases jamming of the feeder mechanism. Normally, the machine components will begin to show signs of wear at about 5000 cycles of operation. At about one million cycle, the feeder plate will have to be replaced, if not sooner. Powdered material will start leaking out from under the feeder box and falling on the rest of the movable components of the machine making maintenance a large problem. Also, the motion of the feeder box will become agitated and impede the free flowing motion of powder during die filling.

In order to overcome the aforementioned problems one needs to search for the right material. Experience indicates that ytrria-doped tetragonal zirconia polycrystal (Y-TZP) ceramic materials offer many advantages over conventional materials, including many other ceramics. Y-TZP is one of the toughest ceramics. The toughness is achieved at the expense of hardness and strength. Tetragonal zirconia alloy-alumina composite, that is, the product of sintering a particulate mixture of zirconia alloy and alumina, is another tough and relatively soft structural ceramic composite. Y-TZP ceramic and zirconia-alumina composites have tribological properties that are not as attractive as other high performance structural ceramics like SiC and Si₃ N₄. However, most of the conventional high performance ceramics are extremely brittle. An example of a material having good hardness and strength is monolithic cubic spinel, however, this material is also highly brittle and is unusable for structural applications.

It is further known that a powder feed assemblage having a feeder box surface, particularly the lower surface of the box in sliding contact with a ware plate surface and die clamp ring has a longer service life and better performance if made with a relatively hard material having high fracture toughness and the mating surfaces have low coefficient friction.

An alternative approach is taught by U.S. Pat. No. 5,358,913, which is hereby incorporated herein by reference. In that approach, a tetragonal zirconia alloy article, which can be near net-shape, is compacted and then sintered in the presence of an MgO, CaO, Y₂ O₃, Sc₂ O₃, Ce₂ O₃, or other rare earth oxide dopant to produce an article having a tetragonal core and a cubic case. The dopant can be provided in a number of different forms such as a solid plate, a powder, or a layer produced by decomposition of an organo-metallic precursor film. In U.S. patent application Ser. No. 07/994,820, now abandoned in favor of Continuation-in-Part application Ser. No. 08/231,870, filed Apr. 25, 1994, a method is described for producing articles having a tetragonal zirconia alloy core and a monoclinic case. In U.S. patent application Ser. No. 07/994,818, now abandoned in favor of a Continuation-in-Part application U.S. Ser. No. 08/400,416, hereby incorporated by reference, a method is described for producing articles having a tetragonal zirconia alloy and α-alumina (alpha-Al₂ O₃) core and a case of tetragonal zirconia and cubic spinel. In the core and the case the predominant species is tetragonal zirconia. The application also teaches a method for producing articles having a core that is tetragonal zirconia alloy along with less than about 5 weight percent alumina and having a case that is cubic phase zirconia and cubic spinel (MgAl₂ O₄). a-alumina is about as hard as cubic zirconia. These types of ceramics with composite structures with varying degrees of physical and mechanical properties are termed as "functionally gradient ceramics". In functionally gradient ceramics, where the core and shell of the ceramic bodies having different crystal structures hereby disclosed in above-referenced U.S. Patents and U.S. Patent Applications.

As will be more completely disclosed, the method of our invention applies to a powder feeder assemblage, i.e., a complete set of stationary ware plate, die clamp ring and sliding feeder box bottom surface made of ceramic and ceramic composites, particularly one type member of the assemblage is made of Y-TZP. If the stationary parts are made of Y-TZP, the sliding part is made of either zirconia-alumina composites or of functionally gradient ceramics based on Y-TZP ceramic or ZrO₂ --Al₂ O₃ composites. Proper choices of ceramics in manufacturing these feeder box, die clamp ring and ware plate assembly are essential to overcome the problems described above.

Therefore, a need persists for an apparatus and method of making precision ceramic powder feed assemblies that have superior wear and abrasion resistance while being cost effective and easy to manufacture.

SUMMARY OF THE INVENTION

It is, therefore, an object of the present invention to provide high precision ceramic die retaining element that is reliable, simple to use and cost effective to manufacture.

It is another object of the invention to provide high precision ceramic die retaining element in which contacting surfaces have remarkably improved wear and abrasion resistance, and therefore, a longer useful life.

It is a feature of the invention that the die retaining element useful for molding equipment comprises selectively tetragonal zirconia ceramic (Y-TZP) or zirconia-alumina composite ceramic.

Accordingly, for accomplishing these and other objects, features and advantages of the invention, there is provided, in an aspect of the invention, an improved die retaining element for securing a die mold in molding equipment in which a powder loading container having a zirconia-alumina ceramic composite sliding portion arranged for reciprocating sliding contact with the die retaining element during loading of the die mold, the die retaining element comprising a flange portion having a tetragonal zirconia polycrystal ceramic sliding portion for slidably contacting the zirconia-alumina ceramic composite sliding portion of the powder loading container.

In another aspect of the invention, an improved die retaining element for securing a die mold in molding equipment in which a powder loading container having a tetragonal zirconia polycrystal ceramic sliding portion arranged for reciprocating sliding contact with the die retaining element during loading of the die mold, the die retaining element comprising a flange portion having a zirconia-alumina ceramic sliding portion for slidably contacting the tetragonal zirconia polycrystal ceramic sliding portion of the powder loading container.

In yet another aspect of the invention, a method of making an improved die retaining element having a ceramic sliding surface, the method comprising the steps of (a) providing a ceramic powder comprising particulate zirconium oxide and a secondary oxide selected from the group consisting of MgO, CaO, Y₂ O₃, Sc₂ O₃, and rare earth oxides, wherein said secondary oxide has a concentration, in the case of Y₂ O₃, about 0.5 to about 5 mole percent; in the case of MgO, about 0.1 to about 1.0 mole percent, in the case of CeO₂, about 0.5 to about 15 mole percent, in the case of Sc₂ O₃, about 0.5 to about 7.0 mole percent and in the case of CaO from about 0.5 to about 5 mole percent, relative to the total of said zirconium oxide, said compacting further comprising forming a blank; (b) providing a mold for receiving and processing said ceramic powder; (c) compacting the ceramic powder in said mold to form a ceramic preform; (d) shaping said ceramic preflorm so as to form a die retaining element having a near net-shaped ceramic sliding surface; (e) sintering said near die retaining element having the near net-shaped ceramic sliding surface thereby forming a sintered ceramic sliding surface; and, (f) further shaping said sintered sliding surface.

It is, therefore, an advantage of the invention that the improved die retaining element having the ceramic sliding surface is reliable, easy to use, cost effective and efficient to practice. Moreover, ceramic die retaining element having the ceramic sliding surface made with the method of the invention imparts low cost to the product, while having characteristically high reliability, a longer life, easier manufacturability, and improved wear and abrasion resistance.

BRIEF DESCRIPTION OF THE DRAWINGS

The above mentioned and other objects, features and advantages of the invention and the manner of attaining them will become more apparent and the invention itself will be better understood by reference to the following description of an embodiment of the invention taken in conjunction with the accompanying drawings, wherein:

FIG. 1 is a perspective view of molding equipment, shown without a die punch, having the die retaining element of the invention;

FIG. 2 is a top plan view of molding equipment having the die retaining element of the invention;

FIG. 3 is a side view of the molding equipment showing the feeder box in the first position along the ware plate;

FIG. 4 is a side view of the molding equipment of the invention showing the feeder box in a second position in contact with the die retaining element;

FIG. 5 is a schematic flow diagram of the method of the invention; and

FIG. 6 is a schematic of a wet bag isostatic pressing machine useful in the method of FIG. 5.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

To overcome the aforementioned problems in the prior art, we carefully manufactured and investigated special ceramic materials for use in the molding equipment 100 of our invention as illustrated in FIG. 1. After considerable investigation and surprise we found that ytrria-doped tetragonal zirconia polycrystal (Y-TZP) ceramic materials offer many advantages over conventional materials, including many other ceramics. Y-TZP is one of the toughest ceramics. The toughness is achieved at the expense of hardness and strength. Tetragonal zirconia alloy-alumina composite, that is, the product of sintering a particulate mixture of zirconia alloy and alumina, is another tough and relatively softer structural ceramic composite.

In FIGS. 1-4, an improved molding equipment 100 according to the principles of the invention is illustrated. Molding equipment 100 has a feeder box 114, for respectively receiving and then discharging powder. Importantly, feeder box 114 has a base, or alternately a first sliding portion, 120, comprising tetragonal zirconia polycrystal ceramic. Base 120 further has a second opening (not shown) for releasing the powder from the feeder box 114 and sidewalls 124 surrounding base 120 for containing the powder. Moreover, molding equipment 100 comprises a ware plate 126 which supports feeder box 114. It is important to the invention that ware plate 126 includes a second sliding portion 128 formed at least partially of a ceramic composite material, as described in details below. Second sliding portion 128 of the ware plate 126 is arranged for sliding contact with the first sliding portion 120 of the base 120 of feeder box 114. Preferably, ware plate 126 is stationary and the first sliding portion 120 of feeder box 114 is slidable along second sliding portion 128 of ware plate 126.

Means, such as a pneumatically controlled ram, 130, is used slidably moving the first sliding portion 120 of the feeder box 114 along the second sliding portion or surface 128 of the ware plate 126. Feeder box 114 is configured to move between a first position where loose powder is fed into the feeder box 114 through, for instance a hopper (not shown), and a second position where the loose powder is released from the feeder box 114 into a die cavity 132, described below.

Die cavity 132 is arranged in the ware plate 126 for receiving a die mold (not shown) into which powder is released by the feeder box 114 when the feeder box 114 is in the second position, as described above. A die retaining element, or alternatively a die retaining ring, 134, is arranged in the die cavity 132 to secure a die mold (not shown) during materials processing. Thus, die retaining ring 134 comes into sliding contact with the first sliding portion 120 of feeder box 114. Moreover, die retaining ring 134 has a third sliding portion or surface 135 arranged in a continuous plane with the ware plate 126 so that feeder box 134 can travel smoothly between the first and second positions. Finally, a die punch 136 is arranged above the ware plate 126 and the second position of the feeder box 114 for accessing the die cavity 132. Thus the die punch 136 can compress the powder released into the die cavity 132 thereby forming the desired molded part.

In a preferred embodiment of the molding equipment 100 of the invention, second sliding portion 128 of ware plate 126 and third sliding portion 135 of die retaining element or ring 134 are each zirconia-alumina ceramic composite; and, first sliding portion 120 of feeder box 114 is tetragonal zirconia ceramic.

In an alternative embodiment of the invention, molding equipment 100 has second sliding portion 128 and third sliding portion 135 of ware plate 126 and die retaining ring 134, respectively, each comprising tetragonal zirconia ceramic; and, the first sliding portion 120 of feeder box 114 comprises zirconia-alumina ceramic composite.

The method of making the improved molding equipment 100 having ceramic elements (described above) is broadly illustrated in FIG. 5 (Steps A to F). According to the method, a ceramic powder comprising of primarily zirconium oxide alloy, or a mixture of particulate zirconium oxide alloy and a second concentration of aluminum oxide is used for making components of ceramic molding equipment, as discussed fully below. Elements of the molding equipment 100 made in accordance with the method of the invention is illustrated in FIG. 5 (Step F) and FIG. 6. The zirconium oxide alloy consists essentially of zirconium oxide and a secondary oxide selected from the group consisting of MgO, CaO, Y₂ O₃, Sc₂ O₃, and rare earth oxides. Moreover, the zirconium oxide alloy has a concentration of the secondary oxide of, in the case of Y₂ O₃, about 0.5 to about 5 mole percent; in the case of MgO, about 0.1 to about 1.0 mole percent, in the case of CeO₂, about 0.5 to about 15 mole percent, in the case of Sc₂ O₃, about 0.5 to about 7.0 mole percent and in the case of CaO from about 0.5 to about 5 mole percent, relative to the total of said zirconium oxide alloy, said compacting further comprising forming a blank. A mold is provided for receiving and processing the ceramic powder. The ceramic powder is then compacted (as described below) in the mold provided to form a ceramic preform. The ceramic preform is then shaped or green-machined so as to form independently near net-shaped green molding components, i.e., first, second and third sliding portions of feeder box, a ware plate, die retaining element, respectively. In this embodiment of the invention, after the initial shaping, the green ceramic molding components are sintered thereby forming a sintered net-shape ceramic molding components, as described more fully below. The ceramic components for the molding equipment 100, described above, are then further machine or shaped until finished components are formed. Subsequently, the components are arranged in the molding equipment 100 as described above.

More particularly, the method of making the molding components, including the first, second and third sliding portions, useful for the molding equipment 100 of the invention, are set forth in details below.

Ceramic Powder Material Mixing

According to FIG. 5, Step A diagrammatically illustrates the alloying process. Zirconia powder 140 is combined with one or more secondary oxide powders 142 to provide zirconia alloy powder 144. The preparation of zirconia alloys is well known to those skilled in the art and zirconia alloys are available commercially. For example, particulate zirconia alloy having 3 mole percent Y₂ O₃ is marketed by Z-TECH Corporation, Bow, N.H., as "SYP-ULTRA 5.2 Yttria Stabilized Zirconia" (presently, HANWHA Advanced Ceramics, as "HWA-3YB") or by TOSOH Corporation of Japan, as "TZ-3YB".

More particularly, we prefer using tetragonal zirconia ceramic material for manufacturing components of the ceramic molding equipment 100 in a cost effective way. The most preferred material which we prefer using is essentially zirconia having 100 percent tetragonal crystal structure. We developed this 100 percent tetragonal zirconia by alloying zirconia with a number of secondary oxides as described in U.S. Pat. Nos. 5,336,282 and 5,358,913, hereby incorporated herein by reference.

The preferred ceramic composite powder mixture most preferred in the method of making zirconia-alumina ceramic composites of the invention includes a particulate zirconia alloy and a particulate alumina made by mixing ZrO₂ and additional "secondary oxide" selected from: MgO, CaO, Y₂ O₃, Sc₂ O₃ and Ce₂ O₃ and other rare earth oxides (also referred to herein as "Mg--Ca--Y--Sc-rare earth oxides") and then with Al₂ O₃. Zirconia alloys useful in the methods of the invention have a metastable tetragonal crystal structure in the temperature and pressure ranges at which the ceramic article produced will be used. For example, at temperatures up to about 200° C. and pressures up to about 1000 MPa, zirconia alloys having, wherein zirconium oxide alloy has a concentration of said secondary oxide of, in the case of Y₂ O₃, about 0.5 to about 5 mole percent; in the case of MgO, about 0.1 to about 1.0 mole percent, in the case of Ce₂ O₃, about 0.5 to about 15 mole percent, in the case of Sc₂ O₃, about 0.5 to about 7.0 mole percent and in the case of CaO from about 0.5 to about 5 mole percent, relative to the total of said zirconium oxide alloy, said compacting further comprising forming a blank and then sintering, exhibit a tetragonal structure. Preferred oxides for alloying with zirconia are Y₂ O₃, MgO, CaO, Ce₂ O₃ and combinations of these oxides. It is preferred that the zirconia powder have high purity, greater than about 99.9 percent. Specific examples of useful zirconia alloys include: tetragonal structure zirconia alloys having from about 2 to about 5 mole percent Y₂ O₃, or more preferably about 3 mole percent Y₂ O₃. Examples of tetragonal structure zirconia alloys useful in the methods of the invention are disclosed in U.S. Pat. No. 5,290,332. Such zirconia alloys are described in that patent as being useful to provide a "net-shape" ceramic article: a ceramic article that is dimensionally true after sintering and, therefore, does not necessitate further machining prior to use in its intended working environment.

Referring again to FIG. 5, Step A' diagrammatically illustrates an alternative mixture of particulate zirconia alloy powder 144 and a particulate aluminum oxide 146. This alternative mixture can be achieved by mixing mechanically or chemically, for example, mixing by co-precipitation. The particulate mixture formed is from about 50 to 100 percent by weight (weight/total weight of particulate mixture) ZrO₂, and preferable is from about 80 to about 99 percent by weight ZrO₂, or more preferably is from about 80 to about 95 percent by weight ZrO₂ and the balance being Al₂ O₃. The product of this alternative mixture produces zirconia-alumina ceramic composite 148.

The grain and agglomeration sizes and distributions, moisture contents, and binders (if any) can be varied in both the alumina and the zirconia alloy, in a manner known to those skilled in the art. "Grain" is defined as an individual crystal, which may be within a particle, having a spatial orientation that is distinct from that of adjacent grains. "Agglomerate" is defined as an aggregation of individual particles, each of which may comprise multiple grains. In a particular embodiment of the invention, the grain and agglomeration sizes and distributions, and moisture contents of the alumina and the zirconia alloy are substantially the same and are selected as if the zirconia alloy was not going to be mixed with the alumina, that is in a manner known to the art to be suitable for the preparation of a zirconia alloy article.

An example of convenient particulate characteristics for a particular embodiment of the invention is the following. Purity of ZrO₂ is preferably well controlled at 99.9 to 99.99 percent, that is, impurities are no more than about 0.1 to 0.01 percent. The grain size is from about 0.1 micrometers to about 0.6 micrometers. The average grain size is 0.3 micrometers. The distribution of grain sizes is: 5-15 percent less than 0.1 micrometers, 40-60 percent less than 0.3 micrometers, and 85-95 percent less than 0.6 micrometers. The surface area of each individual grain ranges from about 10 to about 15 m² /gram or is preferably 14 m² /gram. Agglomerate size is from about 30 to about 60 micrometers and average agglomerate size is: 40-60 micrometers. Moisture content is about 0.2 to 1.0 percent by volume of blank and is preferably 0.5 percent. The mixture of particulate is compacted in the presence of an organic binder.

Referring once again to FIG. 5, Step B, binders such as gelatin or polyethylene glycol(PEG) or acrylic or polyvinyl ionomer or more preferably polyvinyl alcohol, are added to and mixed with the particulate mixture Y-TZP, 144 or a composite mixture of Y-TZP and alumina 148, both illustrated in Step A and A' respectively. This can be achieved preferably by spray drying or ball milling prior to placement of the mixture in a compacting device.

Further, Step B also illustrates an alternative mixing process known to those who are proficient in the art as "compounding" in which the particulate mixture or mixtures are mixed with greater than 20 percent by weight of an organic binder such as paraffin at a temperature higher than the glass transition temperature of such binder for subsequent injection molding process, illustrated as Step C'.

Compacting

Turning now to compacting and more particularly to the exemplary compacting process illustrated in FIG. 5, the particulate mixture either 144 or 148 is cold compacted using preferably an isostatic press 150 (as shown in FIG. 6), to provide an unsintered blank 152 in Step C (FIG. 5). Unsintered blank 152 is alternatively referred to herein as a "green preform". It should be apparent to skilled artisans that a particular method of compacting the powder is not critical. The terms "cold compaction" and the like refer to compression of the particulate mixture at a temperature below glass transition or decomposition temperature of the organic binder. The green preform can be produced by such methods as cold uniaxial pressing (Step C" in FIG. 5), cold isostatic pressing (Step C in FIG. 5), injection molding (Step C'" in FIG. 5) or by processes such as cold extrusion and tape casting(not shown). The particulate mixture is preferably subjected to uniform compacting forces in order to provide an unsintered blank which has a uniform density. Alternatively, near net-shape green blank of the compounds 154 and 156 (of molding equipment 100) arc generated using dry pressing and injection molding processes respectively.

The particulate mixture of zirconia alloy and/or zirconia-alumina ceramic composite is compacted; heated to a temperature range at which sintering will occur; sintered, that is, maintained at that temperature range for a period of time; and then cooled. During all or part of sintering, the particulate mixture compact or the "green preform" is in contact with dopant, as discussed below in detail. In FIG. 5, element 152 represents the product of both mixing chemical species and binders and subsequent compaction, indicated by arrows A, A', B & C', respectively. Compaction and sintering are generally discussed herein as two consecutive operations, as indicated by steps C and E, respectively, in FIG. 5, however, the invention is not limited to a particular sequence of compacting and sintering. For example, compaction and sintering can be simultaneous in a single operation or partial compaction can be followed by sintering and further compaction. The interim product of compacting and sintering operations is referred to herein as a "blank", which is illustrated as element 152 in FIG. 5. Blank 152 is at least partially compacted and is either unsintered or not fully sintered.

In a preferred method of the invention, the powder is cold compacted to provide a "green preform", which has a "green" density that is substantially less than the final sintered density of the ceramic component 160 of molding equipment 100. It is preferred that the green density be between about 40 and about 65 percent of the final sintered density, or more preferably be about 60 percent of the final sintered density.

Referring to FIG. 6, using press 150, the cold isostatic pressing of the powder was done by filling rubber mold 162 with powder 144 or 148 and keeping the mold 162 sealed by plate 164 in autoclave 166 of cold isostatic press 150. Mold 162 is then pressurized to about 25,000 pounds per square inch. Seal plate 164 may either be a metallic material, such as aluminum or steel or a hard rubber. Thus, in accordance with FIG. 5, Step D, near-net-shape components of molding equipment 100 are formed by green machining (as discussed below) of the blank 152 using carbide tools. Then the green components are sintered to full density using preferably sintering schedules described in U.S. Pat. Nos. 5,336,282 and 5,358,913, hereby incorporated hereby by reference, and final precision machining were made to tight tolerances to produce the components of molding equipment of the invention using diamond tools. Near net-shaped green preforms 154 or 156 produced either by dry pressing or by injection molding, respectively, did not warrant green machining to generate net-shaped components after sintering. The near-net-shaped green preform 156 produced by injection molding needed an additional step called "debinding" wherein excess organic binders are removed by heating the preforms at around 250° C. for about 12 hours prior to sintering.

Sintering

Once again referring to FIG. 5, Step E, sintering of the green machined components of molding equipment 100 is performed in a temperature range from about 1400° C. to about 1600° C., or more preferably about 1500° C. Preferable sintering times is in the range from about 1 hour to about 3 hours, or more preferably, about 2 hours. In a particular embodiment of the methods of the invention, the sintering peak temperature is 1500° C. and that temperature is maintained for about 2 hours. It is preferred that the pre-sintered components 158 of molding equipment 100 be slowly heated to sintering temperature and slowly cooled so as to avoid undesirable dimensional changes, distortions and crack development. In an embodiment of the invention having a preferred sintering temperature of 1500° C., preferred temperature ramps during heating are: about 0.3° C./minute for room temperature to about 300° C., about 0.1° C./minute for about 300° C. to about 400° C., about 0.4° C./minute for about 400° C. to about 600° C., and about 1.5° C./minute for about 600° C. to about 1500° C. Preferred temperature ramps during cooling are: about 2° C./minute for about 1500° C. to about 800° C. and about 1.6° C./ininute for about 800° C. to room temperature.

Alternatively, sintering may be achieved in the presence of a dopant selected from: MgO, FeO, ZnO, NiO and MnO, and combination thereof, as discussed below in detail. The resulting zirconia-alumina ceramic composite components of the molding equipment of the invention has a core of α-alumina and tetragonal zirconia and a case of cubic spinel or cubic spinel along with cubic structure or cubic and monoclinic or tetragonal structure of zirconia alloy. For zirconia alloy ceramic, sintering in the presence of dopant selected from "Mg--Ca--Y--Sc-rare earth oxides" will produce articles with cores having tough tetragonal crystal structure and the cases having hard cubic crystal structure.

In the sintering process, the dopant oxide selected from MgO, FeO, ZnO, CoO, NiO, and MnO, and combination thereof, is in contact with the blank. It is preferred that the sintering result in a ceramic components having a "full" or nearly theoretical density, and it is more preferred that the density of the ceramic components be from about 99.5 to about 99.9 percent of theoretical density. Sintering is conducted in air or other oxygen containing atmosphere.

The methods of the invention are not limited to any particular sintering pressure and temperature conditions. Sintering can be performed at atmospheric pressure or alternatively a higher pressure, such as that used in hot isostatic pressing can be used during all or part of the sintering to reduce porosity. The sintering is continued for a sufficient time period for the case of the article being sintered to reach a thermodynamic equilibrium structure. An example of a useful range of elevated sintering pressures is from about 69 MPa to about 207 MPa, or more preferably about 100 to 103 MPa.

The exact manner in which the dopant is in contact with the blank during sintering is not critical, however, the "case" as that term is used herein, is limited to those areas of the blank in contact with the dopant during sintering. For example, a cubic spinel and tetragonal zirconia case can be readily produced by the methods of the invention on a portion of the overall surface of an article. It is not critical that the dopant be in contact with the blank during initial sintering, that is, sintering which does not result in an increase in density to full density.

Prior to observing the results of the examples, the inventors had thought that they would be able to provide an explanation for conversion methods having any relative percentages of zirconia alloy and alumina. The inventors had expected results to be in accord with the concepts that the formation of cubic spinel is highly favored thermodynamically over the conversion of tetragonal zirconia to cubic zirconia and that the mechanism of action follows alumina concentration.

What has been discovered by the inventors is that, surprisingly, if the concentration of alumina in the blank 152 is from about 5 weight percent (relative to the total weight of zirconia and alumina) to about 50 weight percent, then the method of the invention produces an article having a case that is cubic spinel and tetragonal zirconia and a core that is a-alumina and tetragonal zirconia. During sintering, dopant, in effect, diffuses past tetragonal zirconia until all of the dopant has contacted and reacted, i.e., "partitioned", with alumina. In contrast, if the concentration of alumina in the blank is less than about 5 weight percent or greater than about 75 weight percent, then the method of the invention produces an article that has a case that is substantially composted of cubic spinel and cubic zirconia or cubic and monoclinic zirconia and a core that is a-alumina and tetragonal zirconia. During sintering, dopant does not, in effect, diffuse past tetragonal zirconia until all of the dopant has contacted and reacted with alumina; but rather reacts with alumina and tetragonal zirconia in the same vicinity, leaving alumina deeper within the blank unreacted.

These results are not compatible with a simple mechanism of action based on concentration alone. The results seen are compatible with a mechanism of action based upon an unpredictable alignment of several competing factors, such as rate of diffusion of dopant during sintering.

Shaping/Machining

It is known that ceramic parts can be fabricated to net-shape by the compaction processes such as dry pressing, injection molding, slip casting, and extrusion or cold isostatic accompanied by green machining (FIG. 5, Step D). Green machining refers to the process of machining the ceramic particulate compact prior to densification. (For more general information refer to David W. Richardson, Modern Ceramic Engineering: Properties, Processes and Use in Design, 2nd Edition (1992)). In this process, it is important that care be exercised to avoid overstressing the fragile material and producing chips, cracks, breakage, or poor surface. For instance, it is important that the ceramic prefonn is held rigidly, but with no distortion or stress concentration, during green machining. The part can be rigidly held by one of a numerous ways, including by simple mechanical gripping, by bonding or potting with a combination of beeswax and precision metal fixtures, the latter being preferred by the inventors. Once the ceramic preform is secured rigidly in a fixture, green machining can be accomplished in a variety of methods, including: turning, milling, drilling, form wheel grinding, and profile grinding. The inventors prefer turning and profile grinding the preform during green machining to achieve the best results. Machining can be either dry or wet, depending on the binder present and whether or not the part has been bisque fired, i.e., fired at a high enough temperature to form bonds at particle-particle contact points, but not at a high enough temperature to produce densification.

Apart from green machining, a further precision machining Step F, according to FIG. 5, of some of the surfaces is required to meet dimensional tolerances and to achieve improved surface finish or remove surface flaws. Maintaining dimensional tolerances to the extent of few millionths of an inch or achieving surface finish to less than 10 microinches is not possible unless final machining after sintering is undertaken. We accomplished dimensional tolerances to the extent of ±100 millionth of an inch using dry pressing (uniaxial pressing) for parts for simple geometry and controlling the shrinkage by our patented sintering process. Precision machining is required when the part demands tolerances in certain dimensions less than 100 millionth of an inch and also to meet some dimensional tolerances such as roundness, perpendicularity, parallelness, etc. As contrasted with green machining, final precision machining of the sintered ceramic bearing requires diamond tooling and also sophisticated machines. Skilled artisans would know that milling, grinding, lapping and polishing are some effective procedures which are used in precision machining.

This invention is further clarified through the following examples:

WORKING EXAMPLE 1

Zirconia ceramic powder (prealloyed with secondary oxides described in U.S. Pat. Nos. 5,336,282 and 5,358,913) were packed and sealed in molds made of rubber/polyurethane of 55 to 70 durometers of Shore hardness A (preferably 65 durometers). These molds were cold isostatically pressed in an autoclave at 15 to 30 kpsi (preferably 25 kilo pounds per square inch) to obtain preforms of appropriate sizes in width and length.

WORKING EXAMPLE 2

Same as in working Example 1, except that the zirconia alloy powder is premixed with polyvinyl alcohol binder.

WORKING EXAMPLE 3

Same as in working Example 1, except that the zirconia alloy powder is premixed with acrylic binder.

WORKING EXAMPLE 4

Same as in working Example 1, except that the ceramic material is a composite of particulate zirconia alloy and particulate alumina of varying amount of from 5 to 50 weight percent. The binders used in these working examples are the same as that of in the working examples 2 and 3.

WORKING EXAMPLE 5

Preformed blanks produced by cold isostatically pressing are machined in their green state (i.e., before sintering) to produce near-net-shape articles using carbide tools in lathe and milling machines. The cutting speeds in green machining of zirconia preforms were maintained between 2800 and 3400 rpm (preferably at 32,000 rpm).

WORKING EXAMPLE 6

Near net shaped articles of working example 5 were also produced by dry pressing using a die-punch assembly and a cold compacting machine.

WORKING EXAMPLE 7

The green machined near-net-shaped components of the molding equipment made by cold isostatically pressing or near-net-shaped feeder assemblage made by cold pressing are sintered following schedule described in U.S. Pat. Nos. 5,336,282 and 5,358,913. After sintering the ceramic components of the molding equipment achieved full theoretical density of 6.05 gms/cc for yttria stabilized zirconia.

WORKING EXAMPLE 8

The final precision machining of the components of the molding equipment and lapping of the reciprocating motion path were carried out using diamond tools. The surface finish of the feeder assemblage was <0.1 microns.

WORKING EXAMPLE 9

The components of the molding equipment were retrofitted in a powder compacting machine. The powder used for compacting in this machine was of an intermetallic magnetic alloy, more particularly, an alloy of neodymium-boron-iron. This alloy powder is extremely hard and brittle. The components of the molding equipment of this invention survived in excess of ten million cycles of reciprocating motion for powder feed in the die for subsequent compaction.

COMPARATIVE EXAMPLE

The prior art components of the molding equipment for the compacting machine described in the above working example is normally made of hardened steels. When the magnetic alloy powder described in the above working example was used in such machines, the components of the molding equipment did not survive in operation even up to a million cycle.

While the invention has been described with a certain degree of particularity, it is manifest that many changes may be made in the details of the construction and the arrangement of components without departing from the spirit and scope of the disclosure. It is understood that the invention is not limited to the embodiments set forth herein for purposes of exemplification, but is to be limited only by the scope of the attached claim or claims, including the full range of equivalency to which each element thereof is entitled. 

We claim:
 1. A wear and abrasion resistant die retaining element in combination with a contacting surface, said die retaining element comprising a flange portion surrounding a through opening, said flange portion having a tetragonal zirconia polycrystal ceramic sliding portion for reciprocatingly sliding against said contacting surface wherein said contacting surface includes a zirconia-alumina ceramic composite sliding portion.
 2. A wear and abrasion resistant die retaining element in combination with a contacting surface, said die retaining elelment comprising a flange portion surrounding a through opening, said flange portion having a zirconia-alumina ceramic sliding portion for reciprocatingly sliding against said contacting surface wherein said contacting surface includes a tetragonal zirconia polycrystal ceramic sliding portion. 